Acrylic water pressure sensitive adhesive KIWOPRINT D159

KIWOPRINT D159 is a high quality pressure sensitive adhesive for self-adhesive tissue, cardboard, hard PVC,

Rubber, lacquered surfaces, and more. For polyester (PET) and polycarbonate (PC) film sheets, polyethylene (PE)

, polypropylene (PP), glass and metal have good adhesion. KIWOPRINT D 159 has a good non-refundable

Chemical and anti-ultraviolet properties. Due to its soft texture, it is suitable for polyethylene (PE), polypropylene (PP)

And materials such as poly(meth) acrylate (PMMA). Coated KIWOPRINT D 159 as long as appropriate

The storage is dry, dark, cool and covered with silicon paper and can be stored for at least one year without reducing its adhesion.

Usage:

KIWOPRINT D159 can be applied by brush, roller or screen printing. When using screen printing, it must be used

A water-resistant emulsion of the KIWOCOL or AZ0C0L series with a mesh size of 21-43 lines/cm. High mesh

Can improve the printing effect. Stir well before use. If you want to stop printing for more than 10-15 minutes, determine the screen version.

The pressure sensitive adhesive on the gel is removed to prevent the mesh from clogging. The coated pressure sensitive adhesive can be dried at room temperature or through a channel dryer

dry. For processing, the pressure sensitive adhesive should be completely dry and transparent before it can be covered with silicon paper. Before doing any production,

Please test the glue for each combination part such as: printing materials, inks, air cushions, bonding bodies, etc. is suitable. should

It is particularly important to note whether the materials such as the combination portion are suitable for long-term compatibility. Also need to look at the influence and bearing of the air cushion material

The structure or roughness of the printed material. Silicon based release. Plastic surface selection and so on should be noted.

Drying time:

The drying time depends on the amount of pressure sensitive adhesive to be dried, the material to be printed, the drying temperature and the amount of air flow. The following are guidelines for drying at room temperature of 60% relative humidity:

30 μm thick pressure sensitive adhesive: approx. 5 minutes

60μm thick pressure sensitive adhesive: about 8 minutes

90μm thick pressure sensitive adhesive: about 18 minutes

120μm thick pressure sensitive adhesive: about 30 minutes

Dilution : water (up to 5%)

Cleaning : Wet: Water

Dry: PREGAN 1014E

Ingredients : Acrylic composition

Color : Wet: slightly yellow

Dry: transparent

Viscosity : approximately 20,000 mPas (Rheomat STV, meas

Ouring system D II, 20)

Solid content : about 64%

Heat resistance : Approx. -30 ° C to +180 ° C (10 x 2.5 cm attachment area for hand coating on polyester film sheets, undried pressure sensitive

The film layer was 90 μm thick. The polyester sheet is attached to the iron sheet and has a load weight of 30g).

Anti-UV is very good

Peel strength: at least 10 N/inch (1 kp/inch, ASTM BE-T-EX peeling dynamometer. Attachment 2.5x10cm is hand-coated on the polyester film sheet, the undried pressure-sensitive adhesive film layer is 90μm thick) Note: Peel strength depends on

The surface structure of the pressure-sensitive adhesive film layer (different application methods will exhibit different surface structures) and the thickness of the coating.

Viscosity: About 1200 g (Polyken Tack-Tester) was hand-coated on a polyester film sheet, and the undried pressure-sensitive adhesive film layer was 90 μm thick. Note: Due to the different structure of different screens, there will be a lower viscosity in screen printing.

Pz value: about 5

Health hazard / environmental protection: For more detailed information, please consult MSDS

Storage: December (at 20-25 ° C and tightly closed in the original container) KIWOPRINT D 159 should not be exposed to unprotected metal for a long time to prevent frosting.